processing:complex-multi-phase
Differences
This shows you the differences between two versions of the page.
| Both sides previous revision Previous revision | Last revision Both sides next revision | ||
|
processing:complex-multi-phase [2023/12/10 11:10] smerkel [Identify phases and peaks] |
processing:complex-multi-phase [2023/12/10 11:10] smerkel |
||
|---|---|---|---|
| Line 20: | Line 20: | ||
| To do so, it is much better to work on an [[processing:phase_identification| 2θ-histogram of the experimental g-vectors]]. | To do so, it is much better to work on an [[processing:phase_identification| 2θ-histogram of the experimental g-vectors]]. | ||
| - | The figure on the right shows an example from Gay //et al// //Earth and Planetary Science Letters// 604 (2023) [doi: [[https://doi.org/10.1016/j.epsl.2023.118015| 10.1016/j.epsl.2023.118015]]]. The sample holds 4 sample phases and a pressure medium (KCl). Top image is an ω-stack for all experimental g-vectors, potted as a function of ds and η. The bottom image is what you get if you try to index an average diffraction image directly. The middle panel is what is extracted from a 2θ-histogram of the experimental g-vectors. | + | The figure on the right shows an example from Gay //et al//, published in //Earth and Planetary Science Letters// in 2023 [doi: [[https://doi.org/10.1016/j.epsl.2023.118015| 10.1016/j.epsl.2023.118015]]]. The sample holds 4 sample phases and a pressure medium (KCl). Top image is an ω-stack for all experimental g-vectors, potted as a function of ds and η. The bottom image is what you get if you try to index an average diffraction image directly. The middle panel is what is extracted from a 2θ-histogram of the experimental g-vectors. |
| The histogram is less affected by very large grains (the pressure medium in our case). In addition, experimental peak broadening, due to the experiment or the sample properties such as grain size or microstrains, have been removed since we only consider the center of mass of eack peak. | The histogram is less affected by very large grains (the pressure medium in our case). In addition, experimental peak broadening, due to the experiment or the sample properties such as grain size or microstrains, have been removed since we only consider the center of mass of eack peak. | ||
processing/complex-multi-phase.txt · Last modified: 2023/12/10 11:11 by smerkel